No. 27 Anti Graffity Protective Lacquer

Loading...

Description

The Anti Graffity Protective Lacquer is a permanent system for absorbent and nonabsorbent substrates that dries up with satin-finish

Additional information

Container Content

800 ml, 5 Ltr, 10 Ltr

Scope of application

The Anti Graffity Protective Lacquer is a permanent system leaving a satin-finish film on the surface. At the same time, the material protects the substrates against the penetration of water and pollutants. The protective film is de-icing salt resistant according to the WTA-Directive. Daubs and felt-tip pen ink can be removed therefrom several times with our Geiger Anti-Graffity Cleaner (at least 10 to 15 cleaning procedures are possible), before the film must be repaired. The water vapour diffusion ability is not essentially changed (sd-average value 0.6). Anti-Graffity Protective Lacquer can be applied on non-absorbent substrates, such as varnished surfaces, metals, plastics, stone plates and tiles etc., but also on all absorbent surfaces, e.g. facades, plasters, complete heat insulation, concrete, brickwork and natural stones, marble and wood, etc., Critical substrates (such as silicate-based paints) should be pre-treated with No. 28 Adhesive Primer S. Before coating eloxated surfaces with Anti Graffity Protective Lacquer, these, too, have to
be treated with No. 28 Adhesive Primer S. The product is not is not suitable for hydrophobized and water repellent zones and surfaces that are exposed to moisture penetration
(rearward) must not be coated (e.g. free-standing walls).

Fibre cement panels must be coated on all sides, also in area of edges/cutting edges and at the drilling holes. Furthermore, the coating instructions of the panel manufacturers must be observed.

Properties

Free of silicone and wax, thus it can be painted over at any time
permanent system
low SD-value (0.6)
drying up with satin-finish
Tested in accordance with the guideline of Anti Graffti eV and according
to the WTA Directives
Registered in the Bast-List (German Federal Highway Research Institute)

Technical specifications

Make-up ratio: undiluted

Consumption: depending on the substrate 150 to 250 ml/m²